性能项目测试条件测试方法数值/描述单位
机械性能拉伸强度(引张强
度)ASTM D638/IS0
527480(6,800)kg/cm(MPa)[Lb/in2]
断裂伸长率ASTM D638/IS0
527
拉伸模量ASTM D638/IS0
527kg/cm(MPa)[Lb/in2]
拉伸屈服伸长率
(延伸率)ASTM D638/IS0
52720%
拉伸断裂伸长率(延伸丰)ASTM D638/IS0
527%
弯曲模量(弯曲弹
性率)ASTM D790/IS0
17827000(38000)kg/cr(MPa)[Lb/in2]
弯曲强度ASTMD790/IS0
178790(11,660)kg/cm(MPa)[Lb/in2]
洛氏硬度ASTM D785R-116
1ZOD 缺口冲击强
度1/4”23℃ASTM D256/IS0
179kg·cm/cm(J/M)ft·1b/in
1/4”-30℃ASTM D256/IS0
17918(3.3)kg*ca/cm(J/Mft·1b/in
1/8”23℃ASTM D256/IS0
179kg·ca/cm(1/Mft·1b/in
1/8”-30℃ASTM D256/IS0
17920(3.7)kg*cm/cm(1/Mft·1b/in
Charpy 冲击强度23℃ (缺口)ASTM D256/IS0
179kg*cm/cm(J/M)ft·1b/in
-30℃(缺口)ASTM D256/IS0
179kg·cm/cm(J/M0ft·1b/in
23℃(无缺口)ASTM D256/IS0
179kg*cm/cm(J/M0ft·1b/in
-30℃(无缺口)ASTM D256/IS0
179kg*cm/cm(1/M0ft·1b/in
物性性能比重(密度)ASTM D792/IS0
11831.05
成型收缩率ASTM D955
熔融指数(流动
系数)200℃/5kgASTM D1238/IS0
11331.8g/10min
220℃/10kgASTM D1238/IS
113322g/10min
吸水率 23℃/24HASTM D570/IS0
62%
热性能热变形温度退火ASTM D648/ISO
7599(210)℃(下)
未退火ASTM D648/IS0
7588(190)℃(下)
维卡软化点ASTM D1525/1S0
R306105(221)℃(℉)
熔点℃(℉)
燃烧性(率)UL941/16
线性膨胀系数ASTM D696/ISO
11359mm/mm.℃
加工条件干燥条件
加工温度射嘴℃
料筒前段℃
料筒中段℃
料筒后段℃
熔体温度℃
模具温度℃
压力注塑压力Mpa
保压压力Mpa
背压Mpa
螺杆转速rpm
其他备注
颜色
特性高刚性中冲击。电视机前壳/复印机外壳/电话机壳/化妆品盒/轮
胎盖
机械性能拉伸强度(引张强
度)ASTM D638/IS0
527480(6,800)kg/cm(MPa)[Lb/in2]
断裂伸长率ASTM D638/IS0
527
拉伸模量ASTM D638/IS0
527kg/cm(MPa)[Lb/in2]
拉伸屈服伸长率
(延伸率)ASTM D638/IS0
52720%
拉伸断裂伸长率(延伸丰)ASTM D638/IS0
527%
弯曲模量(弯曲弹
性率)ASTM D790/IS0
17827000(38000)kg/cr(MPa)[Lb/in2]
弯曲强度ASTMD790/IS0
178790(11,660)kg/cm(MPa)[Lb/in2]
洛氏硬度ASTM D785R-116
1ZOD 缺口冲击强
度1/4”23℃ASTM D256/IS0
179kg·cm/cm(J/M)ft·1b/in
1/4”-30℃ASTM D256/IS0
17918(3.3)kg*ca/cm(J/Mft·1b/in
1/8”23℃ASTM D256/IS0
179kg·ca/cm(1/Mft·1b/in
1/8”-30℃ASTM D256/IS0
17920(3.7)kg*cm/cm(1/Mft·1b/in
Charpy 冲击强度23℃ (缺口)ASTM D256/IS0
179kg*cm/cm(J/M)ft·1b/in
-30℃(缺口)ASTM D256/IS0
179kg·cm/cm(J/M0ft·1b/in
23℃(无缺口)ASTM D256/IS0
179kg*cm/cm(J/M0ft·1b/in
-30℃(无缺口)ASTM D256/IS0
179kg*cm/cm(1/M0ft·1b/in
物性性能比重(密度)ASTM D792/IS0
11831.05
成型收缩率ASTM D955
熔融指数(流动
系数)200℃/5kgASTM D1238/IS0
11331.8g/10min
220℃/10kgASTM D1238/IS
113322g/10min
吸水率 23℃/24HASTM D570/IS0
62%
热性能热变形温度退火ASTM D648/ISO
7599(210)℃(下)
未退火ASTM D648/IS0
7588(190)℃(下)
维卡软化点ASTM D1525/1S0
R306105(221)℃(℉)
熔点℃(℉)
燃烧性(率)UL941/16
线性膨胀系数ASTM D696/ISO
11359mm/mm.℃
加工条件干燥条件
加工温度射嘴℃
料筒前段℃
料筒中段℃
料筒后段℃
熔体温度℃
模具温度℃
压力注塑压力Mpa
保压压力Mpa
背压Mpa
螺杆转速rpm
其他备注
颜色
特性高刚性中冲击。电视机前壳/复印机外壳/电话机壳/化妆品盒/轮
胎盖